Cranberry Sapphirine Transparent Bullseye Rod 1342
All rods are 42cm in length and 4-5mm diameter. Bullseye is 90COE and isn't compatible with Effetre or Vetrofond Rods. The annealing Temperature range is 505- 520 Celsius.
Contains
Lead
May React With
Selenium, Sulfur
Cold Characteristics
Pale blue to lavender with a hazy sheen.
Working Notes
Torch: 001342-0576 develops a range of streaky pinks in the flame. Work in a cooler, oxidizing atmosphere. May develop a light brown colour on the surface of the glass if worked in the presence of too much propane (or fuel).
Kiln: Rod-only glass style. A linear, streaked design may develop upon firing and may be visible whether fired lengthwise or on end. Colour usually deepens on firing. Possible dark interface reaction with selenium and/or sulphur glasses (000137, 001122, 001125, 000124, 000125, 001137, 001437). Less viscous (softer) than most other glasses. Some gold-bearing striking glasses, like this one, should be fired with a 2-hour hold at 1225°F during the initial stages of the firing cycle. If fired without this hold, they may not strike at all, or they may strike but appear spotty and have a blue-brown cast, as opposed to the desired target colour. This full-fuse schedule effectively strikes these glasses:
| Rate | Temp | Hold |
| * | 1225 | 2:00 |
| 600 | 1490 | :10 |
| 9999 | 900 | ** |
* The initial rate of heat is not a critical factor in successfully striking gold-bearing glasses. Choose an initial rate of heat appropriate to the scale and design of the project that you are firing.
** The remainder of the cycle depends on the thickness of the piece. Consult the Bullseye Annealing Chart. For colour-sensitive projects, we recommend testing the cycle you plan to use by fusing a small sample of a similar setup in the same kiln as the project to best predict final colour results.
Other
Sapphirine is designed to appear light blue in transmission and slightly brown in reflection in its cold state. It is designed to be streaky pink in transmission with slightly brown undertones in reflection after it has been flameworked. We advise labelling all striking glasses.